Study on Flexural Strength and Flexural Failure Modes of Carbon Fiber/Epoxy Resin Composites

Authors

  • Hongwei He College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, P. R. China
  • Kaixi Li Key Laboratory of Carbon Materials, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan, Shanxi, 030001, P. R. China

DOI:

https://doi.org/10.6000/1929-5995.2014.03.01.2

Keywords:

Bending strength, carbon fiber, packing modes, failure mode, composite

Abstract

The flexural failure modes and flexural strength of unidirectional carbon fiber/epoxy (CF/epoxy) composites was theoretically analyzed and calculated. The hypothesis that the maximal flexural strength of unidirectional CF/epoxy composites occurred in outer sheet layer was brought forward. Load-displacement curve of unidirectional CF/epoxy composites also demonstrates that it is correct, which is consistent with the assume. Unidirectional CF/epoxy composites were fabricated with winding and compression molding, and three different kinds of fiber packing modes were proposed and the effects of these modes on flexural prosperities of composites had also been analyzed respectively. Three failure modes, namely fracture of fiber, fracture of epoxy resin and interfacial delamination between fiber and matrix, were analyzed by scanning electron microscopy (SEM). The load-displacement curve of unidirectional CF/epoxy composites indicates the plastic deformation is increased with increasing phenolic resin.

References

Shi YB, Yee AF. Delamination fracture toughness and mechanism of interlayered BMI composites. ICCM 1993; 5: 365-71.

Keppa KL, Sanborn GP, Lacasse PA, et al. Improved fracture toughness of carbon fiber composite functionlized with walled carbon nanotubes. Carbon 2008; 46(15): 2026-33. http://dx.doi.org/10.1016/j.carbon.2008.08.010 DOI: https://doi.org/10.1016/j.carbon.2008.08.010

Yue ZR, Jiang WL. Surface characterization of electrochemically oxidized carbon fibers. Carbon 1999; 7(11): 1785-96. http://dx.doi.org/10.1016/S0008-6223(99)00047-0 DOI: https://doi.org/10.1016/S0008-6223(99)00047-0

Tarantili PA, Andreopoules AG. Mechanical properties epoxies reinforced with chloride-treat aramid fibers. J Appl Polym Sci 1997; 65(2): 267-76. http://dx.doi.org/10.1002/(SICI)1097-4628(19970711)65:2<267::AID-APP7>3.0.CO;2-M DOI: https://doi.org/10.1002/(SICI)1097-4628(19970711)65:2<267::AID-APP7>3.0.CO;2-M

Liu L, Song YJ , Huang YD, et al. The effect of interphase modification on carbon fiber/polyarylacetylene resin composites. Appl Surf Sci 2008; 254(17): 5342-47. http://dx.doi.org/10.1016/j.apsusc.2008.02.078 DOI: https://doi.org/10.1016/j.apsusc.2008.02.078

Xiong XB, Li HJ. Flexural properties of self-graded C/C composite. New Carbon Materials 2001; 16(4): 22-26.

Jiang GL, Peters K. A shear-lag model for three-dimensional unidirectional multilayered structures. Int J Solids Struct 2008; 45(14): 4049-67. http://dx.doi.org/10.1016/j.ijsolstr.2008.02.018 DOI: https://doi.org/10.1016/j.ijsolstr.2008.02.018

Landis CM, Beyerlein IJ, McMeeking RM. Micromechanical simulation of the failure of fiber reinforced composites. J Mech Phys Solids 2000; 48(3): 621-48. http://dx.doi.org/10.1016/S0022-5096(99)00051-4 DOI: https://doi.org/10.1016/S0022-5096(99)00051-4

Xia ZH, Curtin WA. Multiscale modeling of damage and failure in aluminum-matrix composites. Compos Sci Technol 2001; 61(15): 2247-57. http://dx.doi.org/10.1016/S0266-3538(01)00119-1 DOI: https://doi.org/10.1016/S0266-3538(01)00119-1

Xia Z, Curtin WA, Okabe T. Green's function vs. shear-lag models of damage and failure in fiber composites. Compos Sci Technol 2002; 62(10): 1279-88. http://dx.doi.org/10.1016/S0266-3538(02)00073-8 DOI: https://doi.org/10.1016/S0266-3538(02)00073-8

Kun F, Zapperi S, Herrmann HJ. Damage in fiber bundle models. Eur Phys J B 2000; 17(2): 269-79. http://dx.doi.org/10.1007/PL00011084 DOI: https://doi.org/10.1007/PL00011084

Raischel F, Kun F, Herrmann HJ. Failure process of a bundle of plastic fibers. Phys Rev E 2006; 73(6): 66101-12. http://dx.doi.org/10.1103/PhysRevE.73.066101 DOI: https://doi.org/10.1103/PhysRevE.73.066101

Sørensen BF, Jacobesn TK. Large-scale bridging in composites: R-curves and bridging laws. Compos Part A 1998; 29(11): 1443-51. http://dx.doi.org/10.1016/S1359-835X(98)00025-6 DOI: https://doi.org/10.1016/S1359-835X(98)00025-6

Sørensen BF, Jacobesn TK. Crack growth in composites Applicability of R-curves and bridging laws. Plast Rubber Compos 2000; 29(3): 119-33. http://dx.doi.org/10.1179/146580100101540879 DOI: https://doi.org/10.1179/146580100101540879

Yang JJ, Zhang ZG, Cao ZH. Characterization and flexural properties of composites of composites laminates with non-uniform fiber distribution. FRP/Composite 2006; (4): 7-12.

Wang FY, Ma CC, Wu WJ. Mechanical properties, morphology, and flame retardance of glass fiber-reinforced polyamide-toughed novolac-type phenolic resin. J Appl Polym Sci 1999; 73(6): 881-87. http://dx.doi.org/10.1002/(SICI)1097-4628(19990808)73:6<881::AID-APP4>3.0.CO;2-I DOI: https://doi.org/10.1002/(SICI)1097-4628(19990808)73:6<881::AID-APP4>3.0.CO;2-I

Downloads

Published

2014-04-02

How to Cite

He, H., & Li, K. (2014). Study on Flexural Strength and Flexural Failure Modes of Carbon Fiber/Epoxy Resin Composites. Journal of Research Updates in Polymer Science, 3(1), 10–15. https://doi.org/10.6000/1929-5995.2014.03.01.2

Issue

Section

Articles