The Suitability of Seashell, Animal Bone and Sodium Carbonate as Energizers in Case Carburization of Mild Steel
Pages 578-586
O.S. Fatoba, M.A. Bodude, O.L. Akanji, I.O. Adamson and S.C. Agwuncha

DOI: http://dx.doi.org/10.6000/1927-5129.2013.09.74

Published: 01 November 2013

Abstract: This work examines the suitability of using seashell (Oyster shell), animal bone and Na₂CO₃ materials as energizers for case hardening of mild steel. A carburizer consisting of charcoal was used for research with sea shell, animal bone and Na₂CO₃ as energizers. Samples were carburized in fabricated rectangular stainless steel boxes using different percentages of energizers (10, 20, 30, 40, and 50%) respectively. The samples were covered completely in each of the boxes with the mixture of carburizer and energizer placed in the chamber of the furnace. The process was carried out at carburizing temperature of 950⁰C, soaked for 4, 6, and 8hours and quenched in oil. Twenty samples were further tempered at 200⁰C for 1hour to relieve the stress built up during quenching. Hardness test, chemical analysis and impact test were carried out on the samples. The hardness values of the carburized mild steel were measured with a micro hardness tester. The results of the study showed that hardness values of the untempered mild steel samples were slightly improved than the tempered samples at carburizing temperature of 950⁰C and carburizing time of 4, 6 and 8hours. The Impact results revealed that samples carburized at 950⁰C in seashell energizer for 8hours have the highest impact values of 184 Joules for the tempered samples which are higher than the untempered samples due to increase in toughness resulting from tempering. The results also showed that seashell and animal bones are potential energizers in case carburization of mild steel.